采用碱熔融—水浸法从含钨47.14%的酸浸渣中回收钨,考察焙烧温度、焙烧时间、氢氧化钠用量对钨回收率的影响。结果表明,在焙烧温度为700℃、焙烧时间40min、渣与氢氧化钠和碳酸钠的配料比为10∶5∶3时,钨回收率可以达到99.3%。
Abstract：Tungsten was recovered from acid leaching residue bearing 47.14%tungsten by alkali fusion and water leaching.The effects of roasting temperature,roasting time,and dosage of sodium hydroxide on tungsten recovery were investigated.The results show that tungsten recovery rate is 99.35% under the optimum conditions including roasting temperature of 700 ℃,roasting time of 40 min,ratio of slag, NaOH and Na2CO3of 10∶5∶3.
[1]殷丽娟.我国钨资源现状与政策效应[J].中国矿业,2009,18(11):1-3.
[2]孔昭庆.新中国钨工业60年[J].中国钨业,2009,24(5):1-10.
[3]莫似浩.钨冶金的原理和工艺[M].北京:轻工业出版社,1984:29-86.
[4]Charles G Groat.Mineral Commodity Summaries 2002-2009[R].US Department of the Interior,US Geological Survey,Washington:US Government Printing Office,2009.
[5]朱海玲,邓海波,吴承桧,等.钨渣的综合回收利用技术研究现状[J].中国钨业,2010,25(4):16-18.
[6]赵中伟.钨冶炼的理论与应用[M].北京:清华大学出版社,2013:5-9.
[7]万林生,代亚琦,赵立夫,等.高纯钨酸铵溶液中活性炭深度除钼研究[J].中国钨业,2009,24(6):20-22.
[8]鲁伟,徐蕾,余军霞,等.含钨工业废料中提取与分离三氧化钨的研究[J].当代化工,2011,40(1):46-47.
[9]刘宇晖,欧阳宇平,李世勇,等.钨渣处理方法:中国:102212697[P].2011-10-12.
[10]文颖颖.离子交换法从解钼液中分离回收钨钼的研究[D].长沙:中南大学,2000:1-7.
[11]熊炳昆,温旺光,杨新民,等.锆铪冶金[M].北京:冶金工业出版社,2002:65.
[12]郭青蔚,王肇信.现代钽铌冶金[M].北京:冶金工业出版社,2009:198.
[13]张启修,赵秦生.钨钼冶金[M].北京:冶金工业出版社,2005:12
基本信息:
中图分类号:TF841.1
引用信息:
[1]杜阳,马光,吴贤,等.碱熔融—水浸法分离钨的试验研究[J].有色金属(冶炼部分),2014(05):34-37.
基金信息:
国家高技术研究发展计划(863计划)项目(2012AA063204)
2014-05-12
2014-05-12