选用氯化钠脱除铅阳极泥氯化浸出液中的氟硅酸和氟硅酸盐,考察了氯化钠加入量、反应时间、沉降时间、温度等对氟脱除率的影响。在最佳工艺条件下,浸出液中氟浓度可降至2.43g/L以下,除氟率达87.7%。除氟后溶液在蒸馏过程中不产生结晶物,避免蒸馏管道发生堵塞现象,馏出液中氟浓度均在3g/L以下,可以作为稀酸返回浸出。
Abstract：Fluosilicic acid and silicofluoride were removed from chloride leaching solution of lead anode slime by sodium chloride.The effects of sodium chloride dosage,reaction time,precipitation time and temperature on fluorine removal rate were investigated.Fluoride concentration is reduced to 2.43g/L below with fluorine removal rate of 87.7% under the optimum conditions.Crystallization does not occur in defluorination solution during distillation process as to avoid blockage of distillation pipe.Distillate with fluoride concentration of 3g/L meets the requirement of recycling for leaching.
[1]唐谟堂,唐朝波,杨声海,等.用AC法处理高锑低银类铅阳极泥——氯化浸出和干馏的扩大试验[J].中南工业大学学报:自然科学版,2002,33(4):360-363.
[2]鲁君乐,唐谟堂,贺青蒲,等.新氯化—水解法处理铅阳极泥[J].有色金属(冶炼部分),1992(3):21-23.
[3]吴文花,刘吉波,王志坚,等.铅阳极泥中有价金属的分离研究[J].有色金属(冶炼部分),2013(7):47-50.
[4]聂晓军,陈庆邦,刘如意.高锑低银铅阳极泥湿法提银及综合回收的研究[J].广东工学院学报,1996,13(4):51-57.
[5]林宏义.铅阳极泥湿法处理新工艺研究[D].长沙:中南大学冶金科学与工程学院,2004:11-33.
[6]谢斌,胡绪铭.高砷铅泥控制电位氯化浸出金银[J].贵金属,1995,16(1):6-11.
[7]刘万里,王雅斌,谢兆凤,等.脱砷铅阳极泥控电位氯化浸出试验研究[J].有色金属(冶炼部分),2014(6):5-8.
[8]陈进中,曹华珍,郑国渠.高锑低银类铅阳极泥制备五氯化锑新工艺[J].中国有色金属学报,2008,18(11):2094-2099.
[9]郑国渠,陈进中,廖春图,等.一种高锑铅阳极泥湿法处理的方法:中国,201010134248.9[P].2010-03-29.
[10]CAO Hua-zhen,CHEN Jin-zhong,YUAN Hai-jun,et al.Preparation of pure SbCl3 from lead anode slime bearing high antimony and low silver[J].Trans Nonferrous Met Soc China,2010,20(12):2397-2403.
[11]何之华,汪继清,杨文赋.工业磷酸用氯化钠、硅酸钠脱氟的试验研究[J].磷肥与复肥,2009,24(2):21-23.
[12]李建国,李菊梅.氟离子选择电极法在测试中应注意的问题[J].分析试验室,2001,20(1):97-98.
[13]王俊中,魏昶,姜琪.氟硅酸性质[J].昆明理工大学学报:自然科学版,2001,26(3):93-96.
基本信息:
中图分类号:X758
引用信息:
[1]钟扬,陈进中,伍廉奎,等.铅阳极泥氯化浸出液除氟研究[J].有色金属(冶炼部分),2015(10):14-17.
基金信息:
国家“十一五”科技支撑计划项目(2006BAB02B0451); 国家自然科学基金资助项目(51374185)
2015-10-12
2015-10-12