采用不同热处理工艺、不同载荷、不同磨损时间对两种成分(不同相变点)的CuZnAl(RE)形状记忆合金进行了干滑动磨损试验。用TEM和XRD对磨损表面和合金相组成进行了观察与检测。试验结果表明:时效处理的合金耐磨性能优于分级淬火处理的合金,合金相变温度对磨损性能的影响受摩擦副温度与载荷的制约,随载荷增加合金塑性变形增大,使合金表面层破坏而失重,外应力越大,合金塑性变形越大,磨损失重也越大。形状记忆效应和超弹性以及合金的晶粒细化能够明显提高CuZnAl(RE)形状记忆合金的耐磨性。
Abstract：Two kinds of CuZnAl(RE) shape memory alloys(with different phase-transition temperatures) were tested in the condition of dry sliding under different loads,testing times and heat-treatments.The worn surface of the alloy and its phase construction were observed by TEM and XRD.The results indicated that the wear property of CuZnAl(RE) alloy after ageing was better than that of the alloys treated by step quenching.The wear property which was effected by phase-transition temperature of CuZnAl(RE) alloy was related to the temperature of rubbing couples and loads.The plastic deformation of alloys was enlarged with the increase of loads which caused the surface damage and the weight loss of the alloys.The wear resistance of CuZnAl(RE) shape memory alloys could be improved obviously by the shape memory effect,hyperelasticity and grain refinement.
[1]DONG Gui-xia,GU Nan-ju,WANG Bao-qi.Improvingon calculation of martensitetic phenomenological theory[J].Progress in Natural Science,2003,13(7):532-535.
[2]GU Nan-ju,DONG Gui-xia,LIN Xiao-ping.Recent development in crystallographic investigation of martensitic transformation[J].Progress in Natural Science,2004,14(3):193-200.
[3]张进,林晓娉,王宏伟,等.Cu-Al-Mn-Ti形状记忆合金抗母相时效的研究[J].特种铸造及有色合金,2007,27(2):158-160.
[4]司乃潮,赵国旗,杨道清.复合稀土对CuZnAl形状记忆合金力学性能的影响[J].中国有色金属学报,2003,13(2):393-398.
[5]王红卫,吴望子.Cu基形状记忆合金干滑动磨损研究[J].金属学报,1991,27(6):A445-448.
[6]Wang H W,Yang D Z.Friction and wear of unlubricat-ed copper-based CuZnAl shape memory alloys[J].Wear,1991,148:113-121.
[7]王凤庭.CuZnAl形状记忆合金耐磨性研究[J].大连理工大学学报,1991,31(2):245-248.
[8]张思成,徐春园,王建梅.铜合金的干滑动摩擦磨损性能研究[J].甘肃科技,2006,22(2):72-73.
[9]Si Naichao.CuZnAl shape memory alloy refined withcomposite rare earths La+Ce[J].Journal of Rare Earths,1999,17(4):275-279.
[10]司乃潮.CuZnAl(RE)形状记忆合金马氏体稳定化的研究[J].材料研究学报,1999(5):558-560.
[11]徐桂芳,司乃潮,李玉祥.不同组织状态的铜锌铝形状记忆合金滚动磨损性能[J].中国有色金属学报,2004,14(5):825-830.
[12]徐桂芳,司乃潮,李玉祥.热处理工艺对铜锌铝形状记忆合金组织与滚动磨损性能的影响[J].兵器材料科学与工程,2004,27(4):28-32.
基本信息:
中图分类号:TG139.6
引用信息:
[1]司乃潮,刘光磊,司松海,等.工艺因素对CuZnAl(RE)形状记忆合金干滑动磨损性能影响[J].有色金属(冶炼部分),2011(05):47-51+55.
基金信息:
江苏省科技型中小企业技术创新资金项目(BC2007144); 镇江市工业科技攻关项目(GY2007023)
2011-05-15
2011-05-15