对某锌精矿焙砂中性浸出渣进行低酸浸出—矿浆絮凝沉降工艺试验,考察浸出时间、液固比、温度对中性浸出渣低酸浸出和低酸浸出矿浆絮凝沉降的影响。为了模拟工业生产,采用中浸底流与废电解液进行了低酸浸出试验研究,最佳低酸浸出工艺参数下:浸出温度85℃、浸出时间4h、1m3中浸底流废电解液配入量0.84～0.96m3,在上述最佳工艺条件下,矿浆沉降性能良好。
Abstract：Neutral leaching residue of zinc calcine was tested by low acid leaching and flocculation settling of leaching slurry.Effects of leaching time,L/S,and temperature on low acid leaching and flocculation settling were investigated.In order to simulate industrial production,low acid leaching experiments were carried out with neutral leaching underflow and waste electrolyte.Zinc in slag is 20.67%,slag rate of low acid leaching is 46%,and zinc leaching rate is 79.63% under the optimum leaching conditions including leaching temperature of 85℃,leaching time of 4 h,and consumption of waste electrolyte for 1 m3 neutral leaching underflow of 0.84-0.96 m3.
[1]梅光贵，王德润，周敬元，等．湿法炼锌学[M]．长沙：中南大学出版社，2001.MEI G G, WANG D R,ZHOU J Y,et al.Hydrometallurgy of Zinc[M].Changsha:Central South University Press,2001.
[2]王志军，苏立峰，刘三平．新疆某高硅锌焙砂酸浸工艺优化[J]．中国资源综合利用，2018,36(2):19-21.WANG Z J,SU L F,LIU S P.Optimization of acid leaching process of a high silicon zinc in Xinjiang[J].China Resources Comprehensive Utilization,2018,36(2):19-21.
[3]李国民．高硅氧化锌矿浸出脱硅工艺的研究[J]．中国有色冶金，2005,34(4):32-35.LI G M.Research on leaching-desilication process of zinc oxide ore with high silicon[J].China Nonferrous Metallurgy,2005,34(4):32-35.
[4]杨海龙．高硅锌矿水热酸转化及硅聚合沉淀行为研究[D]．昆明：昆明理工大学，2016.YANG H L.Study on hydrothermal acid conversion and silicon polymerization precipitation behavior of high-Si zinc ore[D].Kunming:Kunming University of Science and Technology,2016.
[5]蒋明华．湿法炼锌固液分离理论分析与应用[D]．昆明：昆明理工大学，2002.JIANG M H.Theoretical analysis and application of solid-liquid separation of zinc hydrometallurgy[D].Kunming:Kunming University of Science and Technology,2002.
基本信息:
中图分类号:TF813
引用信息:
[1]刘三平,秦树辰,郑朝振,等.锌焙砂中性浸出渣低酸浸出液固分离试验[J].有色金属(冶炼部分),2020(01):1-4.
基金信息:
国家重点研发计划项目(2018YFC1900400); 国家自然科学基金资助项目(51434001); 国际合作项目(科技部科技伙伴计划资助)(KY201502004); 北京矿冶科技集团有限公司青年创新基金项目(QCJ201823)
2020-01-12
2020-01-12