主要研究了铜钴铁合金掺CaCO3焙烧对合金中钴浸出率的影响。合金分别添加5%、10%、15%、20%的CaCO3在900℃、1 000℃1、100℃、1 200℃、1 300℃下煅烧保温10 h,底层金属富集区与上层渣分离后破碎筛分,溶于H2SO4中。结果表明合金粉在900℃、1 000℃、1 100℃下煅烧时,钴浸出率随CaCO3添加量增加而提高;合金粉添加10%CaCO3在1 300℃下煅烧后浸出,钴浸出率达到峰值,约为95%,其后钴浸出率随CaCO3添加量增加而下降。
Abstract：Effect of roasting by adding CaCO3 during leaching Cu-Co-Fe alloy powder was investigated.Alloy powder,which added CaCO3 individually at the amount of 5% to 20%,was calcined at 9001 300℃ for 10 h.Metal phase was separated from slag,broken,and then dissolved in sulfuric acid.Results show that cobalt leaching rates increased when more CaCO3 was added at 900℃,1 000℃,1 100℃;cobalt leaching rates reached peak value about 95% when alloy powder was roasted at 1 300℃ by adding 10% CaCO3,losses of cobalt during roasting were rapid increased when CaCO3 was more than 10%,leading to lower leaching rate of cobalt.
[1]丰成友,张德全.中国钴资源开发及利用概况[M].矿产与地质,2004,23(1):93-100.
[2]潘彤.我国钴矿矿产资源及其成矿作用[M].矿产与地质,2003,24(4):516-518.
[3]孙晓刚.世界钴资源的分布和应用[J].有色金属冶金,2000(1):38-41.
[4]国土资源科技管理.我国钴资源的特点[J].金川科技,2005(2):38-41.
[5]王海北,刘三平,蒋开喜,等.我国钴生产和消费现状.矿冶,2004,13(3):53-56.
[6]胡宇杰,孙培梅,李洪桂.废硬质合金的回收方法及研究进展[M].稀有金属与硬质合金,2004,32(3):53-57.
[7]王永利,赵丽霞.从含钴废料中提取钴的研究进展[J].再生资源研究,2005(2):29-32.
[8]何章亮,周湘栋.从废催化剂中回收钴和锌的工艺研究[J].中国有色冶金,2004(2):46-48.
[9]兰兴华.用直流电弧炉法从炉渣中回收钴.有色金属[J].2003(5):57-58.
[10]林河成.从含钴催化剂废料中回收氧化钴的研究[J].四川有色冶金,2006(1):12-15.
[11]Leszek A,Zabdyra lga B,Fabrichnayab.Phase equilib-ria in the Co-Cu-O-Si system[J].Computer Coupling ofPhase Diagrams and Thermochemistry,2004,28:293-298.
[12]章四琪,黄劲松.有色金属熔炼与铸锭[M].北京:化学工业出版社,2006.
[13]奥特斯.钢冶金学[M].北京:冶金工业出版社,1997.
[14]Ting T,Katayama G,Tanak A.Distribution BetweenMolten Iron and Slag of the CaO-MgO-FeO-SiO2System[J].Tetsu-to-Hagane,1986,72(2):225-232.
基本信息:
中图分类号:TF816
引用信息:
[1]彭忠东,万文治,胡国荣,等.预处理对铜钴铁合金中钴浸出率的影响[J].有色金属(冶炼部分),2007(06):20-23.
2007-12-12
2007-12-12