在NaCl-KCl-Na2WO4-CuO体系中采用熔盐电解法直接制取钨铜合金粉,并对产物进行了XRD、SEM及EDS分析。结果表明,在780～800℃电解、阴极电流密度106～133mA/cm2、电解时间3～4h、电压2.2～3.2V的条件下,可以得到纯度99%以上、平均粒度0.91μm的钨铜合金粉末,各项指标基本达到了工业上烧结钨铜合金的要求。
Abstract：Tungsten copper alloy powder was directly prepared in NaCl-KCl-Na2WO4-CuO system with molten salt electrolysis.The cathode electrolysis products were analyzed by XRD,SEM and EDS.The results show that copper tungsten alloy powder with purity of above 99% and average particle size of 0.91 μm is obtained under the reaction conditions including electrolytic temperature of 740～820 ℃,cathode current density of 106～133 mA/cm2,electrolysis time of 1.5～3.5 h,cell voltage of 2.2～3.2 V.The product reaches the manufacture requirement of sintering tungsten copper alloy in industry.
[1]German R M,Hens K E,Johnson J L.Powder Metallur-gy Processing of Thermal Management Materials For Micro-electronic Applications[J].Inter.J.of Powder Metallurgy,1994,130(2):205-215.
[2]Hoack D L.用于散热片和电接触器的钨铜复合材料[J].中国钨业,1997,12(1):21-26.
[3]李起培.固体战术导弹燃气舵新材料研究[J].宇航材料工艺,1992(4):78.
[4]陈伟,邝用庚,周武平.中国高温用钨铜复合材料的研究进展[J].稀有金属材料与工程,2004,33(1):11-14.
[5]杨明川,宋贞桢,卢柯.W-20%Cu纳米复合粉的制备[J].金属学报,2004,40(6):639-642.
[6]吕大铭.钨铜材料的生产、应用与发展[J].中国钨业,2004,19(5):1-6.
[7]张明杰,王兆文.熔盐电化学原理与应用[M].北京:化学工业出版社,2006:94-140.
[8]梁英教,车荫昌.无机物热力学数据手册[M].沈阳:东北大学出版社,2008:455-470.
[9]王旭.熔盐电解制备硼及硼化物的研究[D].沈阳:东北大学材料与冶金学院,2009:1-117.
[10]冯威,栾道成,王正云,等.钨铜合金的制备工艺研究[J].西华大学学报:自然科学版,2008,27(1):1-4.
基本信息:
中图分类号:TF123.23
引用信息:
[1]肖志华,廖春发,王旭.熔盐电解法制备钨铜合金粉[J].有色金属(冶炼部分),2013(04):49-52.
基金信息:
国家自然科学基金资助项目(51074081)
2013-04-12
2013-04-12