为实现无铵富集稀土，以复合钠盐为沉淀剂，对铝盐体系离子型稀土矿浸出液中稀土进行富集。考察了pH对稀土浸出液除铝效果的影响，研究了不同沉淀剂、沉淀剂配比及用量、终点pH、反应温度、反应时间、陈化时间对稀土沉淀率的影响。结果表明，在初始稀土浓度0.014 64 mol/L、铝浓度0.54 g/L、初始pH=3.89、反应温度25℃、反应时间60 min的条件下，除铝终点pH=4.93时，残余铝浓度为13.02 mg/L,稀土损失为1.2%;当复合沉淀剂用量为0.7倍理论量的70%NaHCO_3+30%Na_2CO3、沉淀终点pH=6.72、反应时间60 min、反应温度25℃、陈化时间40 min时，稀土沉淀率高达99.68%,灼烧后氧化稀土总量为96.48%,铝含量为0.52%。
Abstract：In order to achieve non-ammonium enrichment of rare earth, complex sodium salt was used as precipitant to enrich rare earth in leachate of ion-type rare earth ore in aluminum salt system.Effect of pH value on removal of aluminum from rare earth leachate was investigated, and effects of different precipitators, ratio and dosage of precipitators, pH value at end point, reaction temperature, reaction time, and aging time on precipitation rate of rare earth were studied.The results show that residual aluminum concentration is 13.02 mg/L,and rare earth loss is 1.2% under the conditions including initial rare earth concentration of 0.014 64 mol/L,aluminum concentration of 0.54 g/L,initial pH value of 3.89,reaction temperature of 25 ℃,reaction time of 60 min, and pH value at end point of 4.93.When the complex precipitator is 70%NaHCO_3+30%Na_2CO3 of 0.7 time of the theoretical amount, end point pH value of precipitation is 6.72,reaction time is 60 min, reaction temperature is 25 ℃,and aging time is 40 min, the rare earth precipitation rate is 99.68%,total amount of rare earth in rare earth oxide is 96.48%,and aluminum content is 0.52%.
[1] 程建忠，车丽萍.中国稀土资源开采现状及发展趋势[J].稀土，2010,31(2):65-69.CHENG J Z,CHE L P.Current mining situation and potential development of rare earth in China[J].Chinese Rare Earths,2010,31(2):65-69.
[2] 黄小卫，李红卫，王彩凤，等.我国稀土工业发展现状及进展[J].稀有金属，2007,31(3):279-288.HUANG X W,LI H W,WANG C F,et al.Development status and research progress in rare earth industry in China[J].Chinese Journal of Rare Metals,2007,31(3):279-288.
[3] 肖燕飞.离子吸附型稀土矿镁盐体系绿色高效浸取技术研究[D].沈阳：东北大学，2015.XIAO Y F.Study on the green and efficient leaching technology for ion-adsorption type rare earths ore with magnesium salt system[D].Shenyang:Northeastern University,2015.
[4] 肖燕飞，黄小卫，冯宗玉，等.镁盐浸出离子吸附型稀土矿的环境影响评价及展望[J].中国稀土学报，2015,33(1):1-9.XIAO Y F,HUANG X W,FENG Z Y,et al.Environmental impact assessment and prospect for ion-adsorption type rare earths ore leaching by magnesium salt[J].Journal of the Chinese Society of Rare Earths,2015,33(1):1-9.
[5] 陈卓.镁盐浸取风化壳淋积型稀土矿浸取过程及工艺优化[D].武汉：武汉工程大学，2018.CHEN Z.Process optimization of weathered crust elution-deposited rare earth ore with magnesium salts[D].Wuhan:Wuhan Institute of Technology,2018.
[6] 王瑞祥，谢博毅，余攀，等.离子型稀土矿浸取剂遴选及柱浸工艺优化研究[J].稀有金属，2015,39(11):1060-1064.WANG R X,XIE B Y,YU P,et al.Selection of leaching agent and optimization of column leaching process of ion-absorbed rare earth deposits[J].Chinese Journal of Rare Metals,2015,39(11):1060-1064.
[7] 王瑞祥，郭跃东，方壮，等.离子型稀土矿硫酸镁柱浸过程中水、稀土和硫酸镁的平衡研究[J].有色金属(冶炼部分),2018(10):36-40.WANG R X,GUO Y D,FANG Z,et al.Equilibrium of water,rare earth and magnesium sulfate in column leaching process of ion-absorbed rare earth deposits[J].Nonferrous Metals (Extractive Metallurgy),2018(10):36-40.
[8] 刘聪，钟化云，李纯，等.一种离子型稀土矿钙盐体系绿色提取方法：CN112176209A[P].2021-01-05.LIU C,ZHONG H Y,LI C,et al.A method for ionic rare earth mineral calcium salt system:CN112176209A[P].2021-01-05.
[9] 朱和玲，张新光.离子型稀土矿氯化钙浸矿模拟与参数优化研究[J].有色金属(矿山部分),2021,73(3):124-128.ZHU H L,ZHANG X G.Simulation and parameter optimization of CaCl2 leaching of ion-type rare earth ore[J].Nonferrous Metals (Mining Section),2021,73(3):124-128.
[10] 陈道贵.离子型稀土矿无铵化浸取剂实验研究[J].矿冶工程，2019,39(2):89-92.CHEN D G.Experimental study on ammonium-free leaching reagent for ion-type rare earthore[J].Mining and Metallurgical Engineering,2019,39(2):89-92.
[11] YU Z H,WANG M,WANG L S,et al.Preparation of crystalline mixed rare earth carbonates by Mg(HCO3)2 precipitation method[J].Journal of Rare Earths,2020,38(3):292-298.
[12] 余宗鹤.硫酸体系碳酸氢镁沉淀制备碳酸稀土过程研究[D].北京：北京有色金属研究总院，2019.YU Z H.Study on the process of preparation of rare earth carbonates by Mg(HCO3)2 precipitation method in sulfuric acid system[D].Beijing:Beijing General Research Institute for Nonferrous Metals,2019.
[13] LUO X P,YUAN X Q,HE K Z,et al.Precipitation process for combined impurity removal from a magnesium sulphate-based leachate of ionic rare earth ore[J].Minerals Engineering,2022,189:107911.DOI:10.1016/j.mineng.2022.107911.
[14] 张臻悦，席银龙，李丹，等.镁盐稀土浸出液稀土沉淀过程[J].有色金属(冶炼部分),2022(5):45-50.ZHANG Z Y,XI Y L,LI D,et al.Precipitation process of magnesium salt rare earth leaching solution[J].Nonferrous Metals (Extractive Metallurgy),2022(5):45-50.
[15] 孟祥龙.低浓度硫酸稀土浸液无氨沉淀富集技术及过程控制[D].北京：北京有色金属研究总院，2017.MENG X L.No-ammonia precipitation enrichment technology and process control of low concentration rare earth sulfate leaching solution[D].Beijing:Beijing General Research Institute for Nonferrous Metals,2017.
[16] 李永绣，黎敏，何小彬，等.碳酸稀土的沉淀与结晶过程[J].中国有色金属学报，1999,9(1):169-174.LI Y X,LI M,HE X B,et al.Precipitation and crystallization process of rare earth carbonate[J].The Chinese Journal of Nonferrous Metals,1999,9(1):169-174.
基本信息:
中图分类号:TF845
引用信息:
[1]胡小洣,刘书祯,袁昌望,等.离子型稀土浸出液复合钠盐高效富集稀土[J].有色金属(冶炼部分),2023(05):52-57.
基金信息:
江西省重点研发计划项目(20202BBGL73116); 江西省教育厅科学技术研究项目(GJJ218517)
2023-05-08
2023-05-08