采用沉淀法制备出磷酸铁,将其与碳酸锂、葡萄糖混合,并掺杂适量的镁,以碳热还原法制备出磷酸铁锂正极材料。制备的磷酸铁粉体D50=2.94μm并呈正态分布。合成的镁掺杂磷酸铁锂颗粒呈类球形,D50=2.80μm;不同镁掺杂量的磷酸铁锂XRD谱没有显著差别。掺杂后的LiFe1-xMg_xPO4/C随着x值的增加,比容量有一定的上升。当x=0.01时,0.1C放电比容量为162mAh/g,1C放电比容量达到135mAh/g,循环性能优异。
Abstract：Ferric phosphate was prepared by precipitation method,and then mixed with lithium carbonate,glucose and magnesium source to prepare lithium iron phosphate by carbothermic reduction method.Particle size of ferric phosphate is normal distribution with D50 =2.94 μm.Mg-doped lithium iron phosphate particles have spherical shape with D50=2.80μm.XRD patterns of synthesized lithium iron phosphate show no significant differences.Specific capacity of LiFe1-xMg_xPO4/C rises with increase of value of x.Upon x=0.01,the discharge capacity of sample is 162 mAh/g at 0.1 Crate and 135 mAh/g at1 Crate respectively.Excellent cycle performance is presented.
[1]邢玉涛.碳包覆磷酸铁锂正极材料的制备及其电化学性能研究[D].北京:清华大学,2013.
[2]罗传喜.新型沉淀法制备高性能磷酸铁锂正极材料研究[D].广州:华南理工大学,2011.
[3]彭忠东,裴振兴,石迪辉,等.快速沉淀—碳热还原法合成亚微米LiFePO4/C[J].电池,2013,43(5):14-17.
[4]LI L,LI X,WANG Z,et al.Stable cycle-life properties of Ti-doped LiFePO4 compounds synthesized by coprecipitation and normal temperature reduction method[J].Journal of Physics&Chemistry of Solids,2009,70(1):238-242.
[5]王震坡,刘文,王悦,等.Mg、Ti离子复合掺杂改性磷酸铁锂正极材料及其电池性能[J].物理化学学报,2012,28(9):2084-2090.
[6]张俊喜,许明玉,曹小卫,等.磷酸铁锂掺杂改性中Li位和Fe位掺杂效果分析[J].功能材料,2011,42(增刊4):699-702.
[7]谷和云,李昇,李二锐,等.镁离子掺杂磷酸铁锂的制备及其电化学性能[J].无机盐工业,2016,48(1):64-67.
[8]冯颖,刘凯,霍涛涛,等.镁掺杂的非化学计量比磷酸铁锂的制备及性能[J].化工进展,2017,36(8):3006-3012.
[9]张培新,文衍宣,刘剑洪,等.镁离子掺杂对磷酸铁锂结构和性能的影响[J].功能材料,2006,37(12):1942-1945.
[10]张俊喜,曹小卫,许明玉,等.Mg2+掺杂的LiFePO4材料的共沉淀合成与表征[J].上海电力学院学报,2009,25(6):547-551.
基本信息:
中图分类号:TM912
引用信息:
[1]李超,刘述平,冯雪茹,等.镁掺杂磷酸铁锂的碳热还原法制备及表征[J].有色金属(冶炼部分),2018(10):60-63.
基金信息:
中国地质调查局地质调查项目(DD20160074)子项目(D1601.6.3)
2018-10-12
2018-10-12