研究了氨—氯化铵体系(NH3-H_2O-NH_4Cl)中含铜铁高的氧化锌矿的浸出行为,探讨了浸出温度、浸出液总氨浓度、浸出时间和液固比对锌浸出率的影响。结果表明,最佳浸出条件为:总氨浓度7.5mol/L、浸出温度50℃、液固比8∶1、浸出时间2h,在最佳浸出条件下锌浸出率达到94.8%。
Abstract：Leaching behavior of high iron & copper bearing lead-zinc ores in ammonia-ammonium chloride(NH3-H_2O-NH_4Cl)system was studied.Effects of leaching temperature,total ammonia concentration,leaching time,and L/S on zinc leaching rate were investigated.The results show that zinc leaching rate is 94.8% under the optimum conditions including total ammonia concentration of 7.5 mol/L,leaching temperature of 50 ℃,L/S of 8∶1,and leaching time of 2 h.
[1]夏志美,陈艺峰,王宇菲,等.低品位氧化锌矿的湿法冶金研究进展[J].湖南工业大学学报,2010,24(6):9-13.
[2]张家靓.MACA法循环浸出低品位氧化锌矿制取电解锌新工艺研究[D].长沙:中南大学,2010.
[3]杨金林,马少健,峰金鹏,等.含铁低品位氧化锌矿石浸出研究[J].广西大学学报,2011,36(6):1042-1047.
[4]杨秀丽,魏昶.某难处理高硅氧化锌矿加压酸浸工艺[J].矿冶工程,2009,29(5):65-69.
[5]HE S,WANG J,YAN J.Pressure leaching of high silica Pb-Zn oxide ore in sulfuric acid medium[J].Hydrometallurgy,2010,104:235-240.
[6]刘三军,欧乐明,冯其明.低品位氧化锌矿石的碱法浸出研究[J].湿法冶金,2005,24(1):23-25.
[7]王瑞祥,唐谟堂.NH3-NH4Cl-H2O体系浸出低品位氧化锌矿制取电锌[J].过程工程学报,2008,8(1):219-222.
[8]夏志美,杨声海,唐谟堂,等.MACA体系中循环浸出低品位氧化锌矿制备电解锌[J].中国有色金属学报,2013,23(12):3455-3460.
[9]唐谟堂,张家靓,王博,等.低品位氧化锌矿在MACA体系中的循环浸出[J].中国有色金属学报,2011,21(1):214-219.
[10]杨声海.Zn(II)-NH3-NH4Cl-H2O体系制备高纯锌理论及应用[D].长沙:中南大学,2003.
基本信息:
中图分类号:TF813
引用信息:
[1]夏志美,金伟,高泽平,等.氧化锌矿浸出试验研究[J].有色金属(冶炼部分),2018(08):1-3.
基金信息:
国家自然科学基金资助项目(51704107,51774127); 湖南省自然科学基金资助项目(2018JJ3142); 湖南省重点实验室开放课题项目(MMA201705); 湖南省高校教学改革研究项目(湘教通[2016]400号)
2018-08-12
2018-08-12