考察碱性硫化钠体系浸出某难处理含锑金精矿过程中金锑分离和综合回收,探讨浸出条件对金和锑浸出的影响,重点对该体系中金的浸出机理进行考察。结果表明,在硫化钠80g/L、氢氧化钠20g/L、常温条件下锑的浸出率达到95.3%,有10.3%的金伴随浸出,同时揭示了金浸出率随电位及温度变化的规律。
Abstract：The separation and comprehensive recovery of gold and antimony from Sb-bearing gold concentrate in alkaline and sodium sulfide system were investigated.The effects of leaching conditions on leaching of gold and antimony were discussed.The gold leaching mechanism in this system was explored.The results show that the leaching rate of antimony at room temperature is 95.3% above accompanied with10.3%leaching rate of gold under the conditions including sodium sulphide of 80g/L and sodium hydroxide of 20g/L.The relationship between gold leaching rate of potential and temperature is revealed.
[1]袁朝新,王云.含砷、锑、碳难处理金精矿焙烧氰化提金工艺研究[J].有色金属(冶炼部分),2003(3):32-34.
[2]李云,袁朝新,王云,等.难处理砷金矿原矿焙烧试验研究[J].有色金属(冶炼部分),2005(2):21-23.
[3]李云,王云,袁朝新,等.提高含砷金精矿两段焙烧焙砂中金浸出率的研究[J].有色金属(冶炼部分),2010(6):33-36.
[4]李云,王云,袁朝新,等.难处理复杂金矿循环流态化焙烧提金技术[J].有色金属(冶炼部分),2011(3):31-33.
[5]黄中省,伍赠玲,邹刚,等.难处理金精矿生物氧化—氰化炭浸法提金试验[J].有色金属(冶炼部分),2011(3):34-38.
[6]李大江.含砷金精矿的酸性热压氧化预处理试验[J].有色金属(冶炼部分),2011(8):28-31.
[7]常耀超,刘大学,王云,等.含砷、锑难处理金精矿提金工艺研究[J].有色金属(冶炼部分),2011(10):31-33.
[8]段东平,周娥,陈思明,等.高砷硫金精矿提金研究[J].有色金属(冶炼部分),2012(1):39-41.
[9]金创石,张廷安,曾勇,等.从难处理金精矿氯化浸金溶液中吸附金[J].有色金属(冶炼部分),2012(3):39-42.
[10]谭希发.难处理金矿的热压氧化预处理技术[J].有色金属(冶炼部分),2012(9):38-43.
[11]赵瑞荣.锑冶金物理化学[M].长沙:中南大学出版社,2003:135-136.
[12]朱国才,方兆衍,陈家镛.多硫化物浸出含金硫化矿的研究[J].贵金属,1994,15(2):26-30.
[13]吴大雄.若干含硫试剂浸金应用基础研究[D].西安:西安建筑科技大学,2003.
[14]朱国才.多硫化物及硫代硫酸盐浸出金体系研究[D].北京:中国科学院化工冶金研究所,1993.
基本信息:
中图分类号:TF803.21
引用信息:
[1]靳冉公,王云,李云,等.碱性硫化钠浸出含锑金精矿过程中金锑行为[J].有色金属(冶炼部分),2014(07):38-41.
基金信息:
“十二五”国家科技支撑计划项目(2012BAB08B04)
2014-07-12
2014-07-12