对SS400钢进行了添加稀土Ce-La合金的试验研究,采用光学显微镜和扫描电镜(SEM)观察和分析钢的晶粒度和夹杂物成分及形貌。结果表明,加入稀土后SS400钢晶粒度提高了1～2级;加入0.05%的稀土Ce-La时,硅酸盐夹杂物近似椭圆形;加入量达到0.09%时,硫化物夹杂和硅酸盐夹杂均呈圆形。
Abstract：The experimental study of adding rare earth Ce-La alloy in SS400 steel was conducted.The grain size,composition and microstructure of inclusion were observed and analyzed in steel with optical microscope and scanning electron microscope(SEM).The results show that grain size of steel enhances 12 levels after adding the rare earth;the silicate inclusion is approximate ellipse with 0.05% addition of rare earth Ce-La,furthermore,the sulfide and silicate inclusion are circular shape when the addition of rare earth Ce-La reaches 0.09%.
[1]周惦武,彭平,徐少华,等.稀土元素在钢中的应用与研究[J].铸造设备研究,2004(3):35-38.
[2]邓小和.稀土镁在SS400钢中的作用机理研究[D].包头:内蒙古科技大学,2008.
[3]秦华,刘丽芳,胡传顺,等.2.25Cr1Mo钢中的夹杂物和晶粒度[J].物理检验:物理分册,2008,44(5):20-22.
[4]Saxena S K,郭新春.采用镁处理生产具有良好力学性能的超洁净钢[J].钢铁钒钛,1998,19(2):64-67.
[5]Wilson W G,Kay D A R,Vaoed A.Use of thermody-namics and phase equilibria to predict the behavior of therare earth elements in steel[J].J Met,1974,26(5):14-23.
[6]杜挺.稀土元素在金属材料中的一些物理化学作用[J].金属学报,1997,33(1):69-77.
基本信息:
中图分类号:TG142.15
引用信息:
[1]杨吉春,聂亚丽,左立杰,等.稀土Ce-La对SS400钢晶粒度及夹杂物变性的影响[J].有色金属(冶炼部分),2012(10):38-41.
基金信息:
国家自然科学基金资助项目(51174114); 内蒙古自治区自然科学基金重点项目(2010Zd105); 内蒙古自治区高校科学研究项目(NJ2207098)
2012-10-12
2012-10-12